Proper Ratio of Lime to Sand

Proper Ratio of Lime to Sand

We hear the question often, “What ratio of lime to sand should I use?” Our answer, “We don’t know what the void space of your sand is.”  There are thousands and thousands of sands across the USA. Within those myriad of sands, there are countless ways that manufactures sieve, wash and process it.

One of our sayings at Lancaster Lime Works is “Sand is not Sand is not Sand.”  The mason’s sand at your local masonry supply company will vary from load to load.  It is of utmost importance to test it for our lime putty for: Void Space/Particle Size/Shape/Distribution.

Our lime putty is the best available. If you add too much or too little lime to your sand, product failure will be the result. We spend just as much time explaining and teaching about sand as we do about installation of lime based mortars

The Basics are Simple:Visual of the Proper Ratio of Lime to Sand
The void space between the sand is similar to the space between beach balls in a display bin.  Between the beach balls there is room for soccer balls, between the soccer balls there is room for baseballs, between the baseballs there is room for marbles, between the marbles there is space for dust. This is the “void space.”

Lime putty must fill the void space within the sand.  Too much lime will push the sand particles apart; not enough lime will leave “holes” in the mortar, and both scenarios will leave you with a weak mortar, stucco or plaster.

Lime Mortars gain the majority of their strength from the sand and rely on the sharp pieces making contact with each other and compacting firmly together. The Lime develops a crystal structure that binds the already sharp, compacted and interlocking particles together.

Portland Cement based mortars are comparable to a two part epoxy glue, they gain the majority of their strength from the binder which is the Portland. Portland “glues” the sand together and negates the necessity for grading and evaluating sand. Lime mortar is a cushion between the building stones or bricks. Portland Cement mortar is a glue that holds the stones or bricks together.

The Correct Ratio:

The ratio of lime to sand is always variable.  Specifications calling for such ratios of 1:2, 1:3 or 1:1 lime to sand are misleading, confusing and could be wrong.  The lime: sand ratio will absolutely vary from sand to sand and from load to load. The correct ratio of lime: sand is determined by discovering the void space within the sand chosen for the project.  Lime putty must fill the void space. Too much lime will push the sand particles apart, not enough lime will leave “holes” in the mortar. Both scenarios leave you with a weak mortar or plaster.

When mixing batches of lime mortar you can easily see the results of a correct ratio.  If the ratio of lime to sand is 1:3 (one lime: three sand), dump three evenly filled buckets of sand into the mixer and one bucket of putty, totaling four buckets.  To confirm you have not added too much lime to the sand, the result will be a total of three buckets of finished lime mortar produced out of the mixer, even though you have added four buckets of material. The putty just fills the space between the sand.

All masons should have the skills to determine void space. They need to prove and explain to architects and engineers the correct amount of lime for the chosen sand.

The testing method of finding the void space between the particles is relatively simple. It is very important to prevent mortar failure and obtain a strong lime mortar.

Lancaster Lime Works provides the training and resources to mason’s and architects in all historic mortars.  Please contact us with questions.